HIPS材料广泛应用各种挤出、注塑类产品中。由于韧性不足，部分HIPS制品存在低温开裂、打螺丝爆裂等问题。我司増韧母料采用高分子量的丁二烯类三元共聚物为主要原材料，改性后经双螺杆挤出造粒，可以有效提高HIPS的冲击强度和拉伸断裂伸长率，解决制品韧性差、脆裂、打螺丝爆裂等问题，添加在HIPS中，有效提高冲击强度，可部分替代ABS制件，降低成本，适用于各种挤出、注塑制品，具有广阔的市场应用前景。
Hips materials are widely used in various extrusion and injection products. Due to lack of toughness, some HIPS products have the problems of low temperature cracking and screw cracking. The Toughening Masterbatch of our company uses high molecular weight butadiene terpolymer as the main raw material. After modification, it is extruded and granulated by twin-screw, which can effectively improve the impact strength and tensile elongation at break of HIPS, solve the problems of poor toughness, embrittlement, screw cracking and other problems of products. When added to hips, it can effectively improve the impact strength, partially replace ABS parts, reduce the cost, and is suitable for extrusion injection molding of various products has a broad market application prospects.
冰箱挤出板材、各类注塑家电制件、HIPS玩具、日用品等的性能提升。
The performance improvement of refrigerator extruded board, all kinds of injection molded home appliances, HIPS toys, daily necessities, etc.
1、熔融指数(200℃，5Kg)：20-50g/10min；
2、提高HIPS的冲击强度并保持其它机械性能基本不变；
3、解决制品韧性差，低温脆裂，打螺丝爆裂等问题；
4、添加在高光HIPS中，提高冲击强度，替代ABS外观件，降低成本；
5、不会影响高光HIPS的光泽度；
6、易添加，可以灵活调整比例，解决不同的韧性问题。
1.MFI (200 ℃, 5kg): 20-50g / 10min;
2. Improve the impact strength of HIPS and keep other mechanical properties unchanged;
3. Solve the problems of poor toughness, low temperature embrittlement, screw bursting, etc;
4. Add in high gloss hips, improve impact strength, replace ABS appearance parts, reduce cost;
5. Does not affect the glossiness of high gloss HIPS;
6. Easy to add, flexible to adjust the proportion, to solve different toughness problems.
ZQ 21499D低成本増韧母粒，效果好，价格低，分散好。
ZQ 21144D増韧着色一体，不用再添加色母料，减少工序，降低成本。
ZQ 21499d low cost Toughening Masterbatch, good effect, low price and good dispersion.
ZQ 21144d is toughened and colored as a whole, and there is no need to add color masterbatch to reduce the process and cost.
向右滑动表格查看更多内容
|
Property |
测试方法 Test method |
测试条件 Test condition |
单位 Unit |
HIPS1173原料 HIPS1173 raw, material |
ZQ21235D |
ZQ21499D |
ZQ2144D |
|
MFR |
ISO 1133 |
200℃, 5 kg |
g/10 min |
/ |
45 |
25 |
20 |
|
Density |
ISO 1183 |
23℃ |
g/m3 |
1.05 |
0.92 |
1.332 |
1.45 |
|
Ash% |
|
|
|
|
0.01 |
28 |
23.5 |
|
拉伸强度Tensile strength |
ISO 527 |
50 mm/min |
MPa |
23.67 |
22.48 |
21.69 |
21.96 |
|
断裂伸长率 Elongation at break |
ISO 527 |
50 mm/min |
% |
80.2 |
83.8 |
79.2 |
80.8 |
|
弯曲强度 Bending strength |
ISO 178 |
2 mm/min |
MPa |
30.32 |
29.97 |
29.38 |
29.65 |
|
弯曲模量 Flexural modulus |
ISO 178 |
2 mm/min |
MPa |
1357 |
1338 |
1319 |
1332 |
|
悬臂梁缺口冲击强度Notched impact strength of cantilever |
ISO 179 |
4mm, 23℃ |
kJ/m2 |
11 |
13.5 |
13.2 |
13.3 |
|
(Note: the product can effectively reduce the cracking rate of refrigerator inner tank after verification by customers. The above data are typical experimental values for reference only（注：产品经客户验证可有效降低冰箱内胆开裂率，上述数据为实验典型值，仅供参考，不作为正式质保承诺。） |
|||||||
使用说明：产品的典型添加比例为4%-10%，客户可以根据増韧实际需求进行适量添加，按需求配比与其他原材料辅料混合均匀后即可使用。
Instructions for use: the typical adding proportion of the product is 4% - 10%. The customer can add appropriate amount according to the actual demand for toughening, and use the product after it is evenly mixed with other raw materials and auxiliary materials according to the demand ratio.
青岛润兴塑料新材料有限公司