产品类别Product Category
|
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途Property and Application |
||||||
|
熔指 MFI g/10min |
密度Density g/cm³ |
拉伸强度 Tensile Strength MPa |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength KJ/m² |
热变形温度HDT（1.80MPa）℃ |
|||
|
ISO 1133 |
ISO 1183 |
ISO 527-2 |
ISO 178 |
ISO 178 |
ISO 180 |
ISO 75 |
|||
|
玻纤增强PA66 GF Reinforced PA66 |
G6605 |
/ |
1.36 |
160 |
230 |
7000 |
10 |
220 |
高强度；应用于结构件 High strength; Applied to structural parts |
|
G6625 |
/ |
1.34 |
150 |
210 |
7000 |
16 |
240 |
优异的耐热性；应用于轨距块专用料 Excellent heat resistance; Applied to gauge block special material |
|
|
玻纤增强PA6 GF Reinforced PA6 |
G5605S |
/ |
1.36 |
150 |
220 |
7000 |
15 |
200 |
高刚、高韧；应用于汽车内饰材料 High stiffness and toughness; Applied to automotive interior materials |
|
PA6-GF30 |
/ |
1.36 |
140 |
190 |
7000 |
12 |
200 |
高强度、耐热老化；应用于发动机周边材料 High strength and heat resistant aging; Applied to engine peripheral materials |
|
|
增韧PA6 Toughening PA6 |
N556 |
/ |
1.10 |
/ |
50 |
1000 |
18 |
150（0.45MPa） |
易成型、易染色；应用于汽车内饰 Easy to shape, easy to dye; Applied to automotive interior |
|
增韧PA66 Toughening PA66 |
N658 |
/ |
1.08 |
40 |
50 |
1000 |
70 |
150（0.45MPa） |
耐热性好；应用于汽车部件 Good heat resistance; Applied to automotive components |
|
阻燃玻纤增强PA66 Flame retardant GF reinforced PA66 |
GRPA66-630B |
/ |
1.42 |
120 |
190 |
7000 |
10 |
230 |
无卤阻燃；应用于电子接插件 Halogen-free flame retardant; Applied to electronic connectors |
|
阻燃玻纤增强PA6 Flame retardant GF reinforced PA6 |
HGRPA6-230 |
/ |
1.58 |
110 |
190 |
7000 |
8 |
190 |
阻燃1.6mm V0；应用于电气部件 Flame-retardant 1.6mm V0;Applied to electrical components |
山东道恩高分子材料股份有限公司
|
产品类别Product Category |
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途Property and Application |
|||||||
|
密度Density g/cm3 |
拉伸强度 Tensile Strength MPa |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength J/m
|
热变形温度HDT（1.82MPa）℃ |
阻燃性 Flame retardance
|
||||
|
ASTM D792 |
ASTM D638 |
ASTM D790 |
ASTM D256 |
ASTM D648 |
UL 94 |
|||||
|
玻纤增强PA6 Glass reinforced PA6 |
RF-6001G15 |
1.23 |
110 |
160 |
5000 |
80 |
180 |
HB |
玻纤增强PA6、童车配件 GF reinforced PA6, Stroller accessory |
|
|
RF-6001G20 |
1.27 |
130 |
190 |
6000 |
100 |
190 |
HB |
玻纤增强PA6、电动工具 GF reinforced PA6,electric tool |
||
|
RF-6001G25 |
1.31 |
150 |
220 |
7000 |
115 |
200 |
HB |
玻纤增强PA6、公交座椅 GF reinforced PA6 ,bus seat |
||
|
RF-6001G30 |
1.36 |
175 |
250 |
8000 |
150 |
205 |
HB |
玻纤增强PA6，汽车风扇 GF reinforced PA6,automobile cooling fan |
||
|
RF-6001G30-X |
1.36 |
110 |
190 |
6500 |
110 |
200 |
HB |
低成本玻纤增强，滑板车 Low-cost GF reinforced PA6 |
||
|
RF-6001G35 |
1.41 |
180 |
260 |
9000 |
150 |
205 |
HB |
玻纤增强PA6，电动工具 GF reinforced PA6, electric tool |
||
|
RF-6001G50 |
1.56 |
200 |
280 |
11000 |
160 |
215 |
HB |
高玻纤增强，手机支架 High GF reinforced, cellphone holder |
||
|
RF-60011G65 |
1.68 |
210 |
310 |
13000 |
170 |
220 |
HB |
高玻矿增强、户外用品 High GF reinforce, outdoor products |
||
|
增韧PA6 Toughened PA6 |
TH-6001 |
1.09 |
60 |
80 |
1500 |
200 |
60 |
HB |
增韧，耐低温，体育用品 Toughened, low temperature resistant, sports goods |
|
|
TH-6002 |
1.05 |
55 |
60 |
1500 |
750 |
55 |
HB |
超韧，耐低温，体育用品 Super-toughened, low temperature resistant, sports goods |
||
青岛海尔新材料研发有限公司
|
产品类别Product Category |
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途Property and Application |
|||||||
|
密度Density g/cm3 |
拉伸强度 Tensile Strength MPa |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength J/m
|
热变形温度HDT（1.82MPa）℃ |
阻燃性 Flame retardance
|
||||
|
ASTM D792 |
ASTM D638 |
ASTM D790 |
ASTM D256 |
ASTM D648 |
UL 94 |
|||||
|
阻燃PA6 Flame retarded PA6 |
FR-6003 |
1.33 |
70 |
120 |
3500 |
35 |
100 |
V0 |
溴系阻燃，电器接插件 Bromine flame retardants, electrical connections |
|
|
NH-6004 |
1.19 |
60 |
90 |
2800 |
40 |
60 |
V0 |
无卤阻燃，电器接插件 HFFR, electrical connections |
||
|
NH-6024 |
1.18 |
70 |
110 |
3000 |
60 |
70 |
V2 |
无卤阻燃、低端接插件 HFFR, low-end electric connections |
||
|
溴系阻燃增强PA6 Brominated flame-retarded & reinforced PA6 |
FR-6003GX |
1.58 |
140 |
210 |
8500 |
80 |
205 |
V0 |
高阻燃高CTI、电机骨架 High flame retardancy and high CTI, motor skeleton |
|
青岛海尔新材料研发有限公司
|
产品类别Product Category |
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途Property and Application |
||||||
|
熔指 MFI g/10min |
密度Density g/cm3 |
拉伸强度 Tensile Strength MPa |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength J/m
|
热变形温度HDT（1.82MPa）℃ |
|||
|
ASTM D1238 |
ASTM D792 |
ASTM D638 |
ASTM D790 |
ASTM D256 |
ASTM D648 |
||||
|
红磷阻燃增强PA6 Phosphorus flame-retarded & reinforced PA6 |
NH-6014G30 |
1.39 |
140 |
220 |
8000 |
125 |
205 |
V0 |
阻燃增强、电器外壳 Flame-retardant reinforcement, electrical cover |
|
NH-6014G30B |
1.36 |
125 |
160 |
7200 |
140 |
195 |
V0 |
高阻燃耐低温，电器外壳 High flame retardancy low temperature resistance, electrical cover |
|
|
NH-6014B30L |
1.36 |
120 |
160 |
7500 |
120 |
190 |
V0 |
低成本阻燃增强电器外壳 Low cost flame retardant reinforced electrical cover |
|
|
NH-6014G40 |
1.49 |
160 |
230 |
9000 |
130 |
205 |
V0 |
红磷阻燃增强，电器外壳 Red phosphorus flame retardant reinforced, electrical cover |
|
|
NH-6014G40B |
1.43 |
145 |
180 |
8500 |
140 |
195 |
V0 |
耐低温高阻燃，电器外壳 Low temperature and high flame retardancy, electrical cover |
|
|
通用注塑级PA6 PA6 for General injection molding |
H2700N |
1.14 |
70 |
90 |
170 |
50 |
85 |
V0 |
高光注塑级 High luster injection molding grade |
|
波纹管专用PA6 PA6 for corrugated pipe |
FR-600D |
1.30 |
65 |
80 |
1300 |
200 |
70 |
V0 |
热老化D级波纹管专用料 Special material for bellows, thermal aging grade D |
|
耐磨PA6 Wear-resisting PA6 |
RF-7301 |
1.24 |
80 |
110 |
2500 |
150 |
180 |
V0 |
芳纶增强耐磨，轴套齿轮 Aramid reinforced, wear resistance, shaft gear |
青岛海尔新材料研发有限公司
|
产品类别Product Category |
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途 Property and Application |
|||||||
|
密度Density g/cm3 |
拉伸强度 Tensile Strength MPa |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength J/m
|
热变形温度HDT（1.82MPa）℃ |
阻燃性 Flame retardance
|
||||
|
ASTM D792 |
ASTM D638 |
ASTM D790 |
ASTM D256 |
ASTM D648 |
UL 94 |
|||||
|
玻纤增强PA66 GF reinforced PA66 |
RF-7001G15 |
1.23 |
115 |
165 |
5200 |
75 |
210 |
HB |
玻纤增强PA66，接插件 Glass fiber reinforced PA66, connector |
|
|
RF-7001G20 |
1.27 |
140 |
200 |
6500 |
95 |
235 |
HB |
玻纤增强PA66，电子电器 Glass fiber reinforced PA66 electronics |
||
|
RF-7001G25 |
1.31 |
160 |
230 |
7500 |
105 |
250 |
HB |
玻纤增强PA66，电动工具 Glass fiber reinforced PA66, electric tools |
||
|
RF-7001G30 |
1.36 |
185 |
255 |
8500 |
115 |
250 |
HB |
玻纤增强PA66，汽车水室 Glass fiber reinforced PA66, Auto water chamber |
||
|
RF-7001G35 |
1.41 |
195 |
270 |
9700 |
135 |
250 |
HB |
玻纤增强PA66，汽车水室 Glass fiber reinforced PA66, Auto water chamber |
||
|
RF-7001G50 |
1.56 |
190 |
250 |
13000 |
130 |
250 |
HB |
玻矿增强PA66，家电铰链 Glass fiber reinforced PA66 Home appliance hinge |
||
|
增韧PA66 Toughened PA66 |
TH-7001 |
1.09 |
60 |
75 |
1800 |
200 |
70 |
HB |
增韧耐低温，体育用品 Toughened and low temperature resistance,sporting goods |
|
|
TH-7002 |
1.05 |
45 |
60 |
1600 |
750 |
60 |
HB |
超韧耐低温，体育用品 Super toughness and low temperature resistance, sporting goods |
||
|
阻燃PA66 Flame retarded PA66 |
FR-7003 |
1.33 |
75 |
130 |
3600 |
35 |
105 |
V0 |
溴系阻燃，电器接插件 Bromine flame retardant, electrical connectors |
|
|
NH-7004 |
1.19 |
65 |
95 |
2900 |
40 |
65 |
V0 |
无卤高阻燃，电器接插件 Halogen-free high flame retardant electrical connectors |
||
|
溴系阻燃增强PA66 Brominated flame-retarded & reinforced PA66 |
FR-7003G30 |
1.58 |
150 |
250 |
9000 |
80 |
250 |
V0 |
高阻燃高CTI，电机骨架 High flame retardancy and high CTI, moto skeleton |
|
青岛海尔新材料研发有限公司
|
产品类别Product Category |
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途 Property and Application |
|||||||
|
密度Density g/cm3 |
拉伸强度 Tensile Strength MPa |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength J/m
|
热变形温度HDT（1.82MPa）℃ |
阻燃性 Flame retardance
|
||||
|
ASTM D792 |
ASTM D638 |
ASTM D790 |
ASTM D256 |
ASTM D648 |
UL 94 |
|||||
|
红磷阻燃增强PA66 Phosphorus flame-retarded & reinforced PA66 |
NH-7014G25 |
1.35 |
140 |
220 |
7500 |
90 |
250 |
V0 |
红磷阻燃增强，电器外壳 Red phosphorus flame retardant reinforced, electrical cover |
|
|
NH-7014G25B |
1.32 |
125 |
180 |
6000 |
120 |
235 |
V0 |
红磷阻燃增强，电器外壳 Red phosphorus flame retardant reinforced, electrical cover |
||
|
NH-7014G35 |
1.46 |
160 |
240 |
8000 |
125 |
250 |
V0 |
红磷阻燃增强，电器外壳 Red phosphorus flame retardant reinforced, electrical cover |
||
|
NH-7014G35B |
1.43 |
145 |
185 |
7000 |
140 |
235 |
V0 |
超韧耐低温，电器外壳 Super toughness and low temperature resistance, electrical cover |
||
|
通用注塑级PA66 PA66 for general injection molding |
H1300 |
1.14 |
75 |
95 |
2500 |
60 |
80 |
HB |
高光通用注塑级 High luster general injection molding grade |
|
|
碳纤增强PA66 CF reinforced PA66 |
CF-6001 |
1.34 |
230 |
260 |
15000 |
140 |
255 |
HB |
碳纤增强鱼竿电动车曲轴 Carbon fiber reinforced ,fishing rod ,motor crankshaft |
|
青岛海尔新材料研发有限公司
|
产品类别Product Catagory |
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途 Property and Application |
|||||||
|
密度Density g/cm³ |
拉伸强度 Tensile Strength MPa |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength J/m |
热变形温度HDT（1.80MPa）℃ |
阻燃性 Flame retardant |
||||
|
ASTM D792 |
ASTM D638 |
ASTM D790 |
ASTM D256 |
ASTM D648 |
UL 94 |
|||||
|
玻纤增强PA6 GF reinforced PA6 |
DA616 |
1.36 |
150 |
220 |
8000 |
120 |
200 |
HB |
30%玻纤增强PA6
30% Fiber Reinforced Seats of bus |
|
|
增韧PA6 Toughened PA6 |
NA610 |
1.12 |
60 |
80 |
2400 |
120 |
60 |
HB |
增韧PA6，耐低温
Toughened PA6, low temperature resistance sports equipment |
|
|
增韧PA6 Toughened PA6 |
NA612 | 1.10 | 60 | 78 | 2100 | 130 | 70 | HB |
增韧PA6，耐低温 Toughened PA6, low temperature resistance 体育用品 sports equipment |
|
|
玻纤增强PA66 GF reinforced PA66 |
DA716 |
1.36 |
165 |
255 |
8500 |
110 |
250 |
HB |
30%玻纤增强PA66
30% Fiber Reinforced auto radiator water chamber |
|
|
增韧PA66 Toughened PA66 |
KD6624 |
1.12 |
75 |
100 |
2800 |
120 |
70 |
HB |
增韧PA66，耐低温
Toughened PA66, low temperature resistance sports equipment |
|
|
增韧PA66 Toughened PA66 |
KD6627 |
1.09 |
60 |
75 |
1800 |
200 |
70 |
HB |
超韧PA66，耐低温
Super toughened PA66, low temperature resistance sports equipment |
|
|
阻燃玻纤增强PA6 Flame retardant GF reinforced PA6 |
PE718F0 |
1.48 |
140 |
210 |
7800 |
80 |
230 |
V0 |
高阻燃高CTI
High flame retardancy, high CTI Motor frame |
|