产品类别Product Category |
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途Property and Application |
||||||
|
熔指 MFI g/10min |
密度Density g/cm³ |
拉伸强度 Tensile Strength MPa |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength KJ/m² |
热变形温度HDT（1.80MPa）℃ |
|||
|
ISO 1133 |
ISO 1183 |
ISO 527-2 |
ISO 178 |
ISO 178 |
ISO 180 |
ISO 75 |
|||
|
PBT |
PBT425NP |
/ |
1.30 |
50 |
60 |
2000 |
3 |
130（0.45MPa） |
强度高、易成型；应用于车灯装饰框、汽车部件 High strength, easy to process; Applied to decorative frame of headlamp and auto parts |
|
阻燃增强 Flame retardant enhanced PBT
|
HGRPBT-230 |
/ |
1.67 |
100 |
170 |
8000 |
8.5 |
190 |
强度高、阻燃性能好；应用于电子接插件 High strength, good flame retardancy ;Applied to electronic connectors |
|
GF4876LW-A BK |
/ |
1.64 |
120 |
160 |
7000 |
8 |
170 |
低气味；应用于家电外壳 little odor;Applied to the housing of home appliance |
|
|
增强PBT Reinforced PBT |
PBT-GF30 |
/ |
1.53Z |
120 |
190 |
7000 |
8 |
190 |
高强度、高耐热；应用于汽车部件 High strength and heat resistance; Applied to automotive components |
山东道恩高分子材料股份有限公司
|
产品类别Product Category |
牌号Grade |
测试标准、测试项目 Test Criteria, Test Items |
特性及用途 Property and application |
||||||
|
熔指 MFI g/10min |
洛氏硬度 Rockwell hardness |
断裂伸长率 Elongation at break % |
弯曲强度 Flexural Strength Mpa |
弯曲模量 Flexural modulus Mpa |
悬臂梁缺口冲击强度 Notched Izod impact strength J/m
|
阻燃性 Flame retardance
|
|||
|
ASTM D1238 |
ASTM D785 |
ASTM D638 |
ASTM D790 |
ASTM D256 |
UL 94 |
||||
|
玻纤增强PBT GF reinforced PBT |
RF8001G15 |
20，250℃，2.16kg |
118 |
8 |
150 |
4700 |
70 |
HB |
增强高耐热，马达端盖 Reinforced high heat resistance, motor end cover |
|
RF8001G20 |
17，250℃，2.16kg |
118 |
7 |
170 |
5600 |
90 |
HB |
增强高耐热，汽车零部件 Reinforced high heat resistance, automotive parts |
|
|
RF8001G30 |
12，250℃，2.16kg |
117 |
7 |
190 |
7500 |
110 |
HB |
增强高强度，工业品零件 Reinforced high strength, industrial parts |
|
|
阻燃增强PBT Flame retarded reinforced PBT |
FR8003G15 |
15，250℃，2.16kg |
118 |
6 |
140 |
4400 |
55 |
1.5mm V0 |
增强高阻燃，冷却风扇 Enhanced high flame retardant, cooling fan |
|
FR8003G20 |
13，250℃，2.16kg |
118 |
6 |
155 |
5500 |
70 |
1.5mm V0 |
增强高阻燃，线圈骨架 Enhanced high flame retardant, coil skeleton |
|
|
FR8003G30 |
10，250℃，2.16kg |
117 |
6 |
185 |
8800 |
90 |
1.5mm V0 |
增强高阻燃，连接器 Enhanced high flame retardant, connectors |
|
青岛海尔新材料研发有限公司